SNT-8042 casting repair agent

Your current locations: Home >> Products >> Industrial repair agent

SNT-8042 casting repair agent

  • category:Industrial repair agent

  • The number of clicks:
  • Release date:2017/09/27
  • Online inquiry
Details

SNT-8042 casting defect repair agent is a variety of alloy materials and modified toughening resin composite high-performance polymer materials. Two-component, gray rubber-like, for the color requirements are not too strict repair of various casting defects.

SNT-8042 Casting defect repair agent product characteristics

1, after curing the material has a high strength, can be all kinds of mechanical processing.

2, a wide range of applications for a variety of metal defects in the repair and regeneration.

3, with wear resistance and anti-aging characteristics.

LT101 casting defect repair product parameters

SNT-8042 Casting defect repair agent

product name

Colour

status

package

volume

(cm3)

Operating time limit

(25℃)

Curing time

(25℃)

gray

Paste

500g

303

25min

18h


density

(g/cm3)

Compressive strength

(kg/cm2)

GB1041-2008

Tensile Strength

(kg/cm2)

GB6329-1999

Shear strength

(kg/cm2)

GB7124-2009

Bending strength

(kg/cm2)

GB1042-2008

hardness

(Shore D)

ASTM-D-2556

Operating temperature

(℃)

1.54

865

291

181

486

87

-60~150

Instructions

     1, surface treatment: to repair the surface roughening treatment and cleaning with a cleaning agent.

     2, the preparation: according to the mass ratio of A: B = 2: 1 SNT-8042 casting defect repair agent mixed evenly, and within the specified operating time limit.

     3, coating: mixed with a good casting defect repair agent layer by layer in the repair area, the first layer to be compacted, so that the full infiltration with the substrate. Such as after the order to be mechanical processing, to set aside the amount of processing margin.

     4, curing: 25 ~ 30 ℃ curing 8 hours can be machined, 18 hours after use.

   Precautions

     1, the temperature below 15 ℃, should take appropriate heating measures, or should extend the curing time.

     2, when the ambient temperature is high or larger amount of plastic when the operating time will be shortened.

     3, the goods in a cool dry environment sealed storage, shelf life of 2 years; by non-dangerous goods transport.

     4, the goods are non-dangerous goods, but do not import and eyes, to avoid long-term direct contact with the body.