SNT-901 wear-resistant repair agent

Your current locations: Home >> Products >> Wear-resistant coating

SNT-901 wear-resistant repair agent

  • category:Wear-resistant coating

  • The number of clicks:
  • Release date:2017/09/27
  • Online inquiry
Details

This product is a variety of high-performance wear-resistant, corrosion materials (such as ceramics, silicon carbide, emery, titanium alloy) and modified toughened heat-resistant resin composite high-performance wear-resistant polymer ceramic materials. Used to accurately repair the friction and wear failure of the journal, shaft hole, bearing and other parts.

Performance characteristics

☆ wear resistance is excellent, is more than 2 times the general metal.

☆ with a variety of metal substrates have a high bond strength;

☆ construction technology is good, curing without shrinkage;

☆ After curing the material has a very high strength, can be all kinds of mechanical processing;

Instructions

1, the surface treatment: repair parts of the coarsening treatment, such as the conditions allowed to drive about 1.5mm deep 縲 pattern, and then cleaning agent to clean.

2, the preparation: according to the mass ratio of A: B = 4: 1 A, B two components mixed evenly, and within the specified operating time limit.

3, coating: the mixed material will be coated layer of coating in the repair area, the first layer to be compact, so that the full infiltration with the substrate. Such as after the order to be mechanical processing, to set aside the amount of processing margin.

4, curing: 20 ~ 25 ℃ curing 8 hours can be machined, can be put into use after 24 hours, if the temperature should be used to heat or prolong the curing time to promote curing.

Performance parameters

SNT901 Wear Resistant Patch Physical and Mechanical Properties

Colour

Physical state

density(g/cm3)

Compressive strength(kg/cm2)
GB/1041-2008

Shear strength(kg/cm2)
GB/7124-2008

Tensile Strength(kg/cm2)
GB6329-2009

Bending strength(kg/cm2)
GB1042-1999

hardness(Shore D)
ASTM-D-2556

black

Paste

1.54

1428

281

573

646

93

 

SNT901 wear-resistant repair agent curing characteristics table(Test conditions: temperature 20 ~ 25 ℃, relative humidity 55)


Operable time limit(min)

Curing time

Full curing time before running

To ensure wear resistance of the operating temperature(℃)


30

Room temperature 24h or Room temperature 2h+80℃1h

48h

-60~150


Special Note 

1, the parameters for the laboratory conditions, due to the actual conditions are more complex, it is recommended that users do pre-test according to the actual conditions.

2, when the ambient temperature below 15 ℃, the curing time will be extended, should take appropriate heating measures;

3, when the ambient temperature is higher than 25 ℃ or mixing is too large, the curing speed will be accelerated, to properly shorten the mixing time.

Transport storage

Cool and dry place sealed storage, shelf life of 2 years. Transport to avoid inversion, to avoid bumps, according to non-dangerous goods transport.