SNT-899 metal repair agent

Your current locations: Home >> Products >> Industrial repair agent

SNT-899 metal repair agent

  • category:Industrial repair agent

  • The number of clicks:
  • Release date:2017/09/27
  • Online inquiry
Details

  SNT-899 metal repair agent is a variety of alloy materials and modified toughening heat-resistant resin composite high-performance polymer materials. Two-component, clay-like, color and carbon steel is basically the same. Wear resistance and bonding strength, comprehensive mechanical properties. For a variety of carbon steel, alloy steel, stainless steel and other casting defects repair and parts wear, scratches, corrosion, fracture repair. After repair the color and the substrate is basically the same, with high strength, and excellent wear resistance and anti-aging properties, and with the substrate with a variety of mechanical processing.

  SNT-899 steel repair agent product parameters

product nameColourstatuspackagevolume(cm3)Operating time limit(25℃)Curing time(25℃)
SNT-899 steel repair agentSteel colorPaste500g29830min24h


density(g/cm3)Compressive strength(kg/c㎡)GB1041-2008Tensile Strength(kg/c㎡)GB6329-1999Shear strength(kg/c㎡)GB7124-2009Bending strength(kg/c㎡)GB1042-2008hardness(Shore D)ASTM-D-2556Operating temperature(℃)
1.64106439126558293-60~170


Use of SNT-899 steel repair agent

   1, surface treatment: to repair the surface roughening treatment and cleaning with a cleaning agent.

   2, preparation: according to the mass ratio of A: B = 4: 1 SNT-899 metal repair agent mixed evenly, and within the specified operating time limit.

   3, coating: the mixed material will be coated layer of coating in the repair area, the first layer to be compact, so that the full infiltration with the substrate. Such as after the order to be mechanical processing, to set aside the amount of processing margin.

   4, curing: 25 ~ 30 ℃ curing 24 hours can be machined, 18 hours after use.

Precautions

   1, the temperature below 15 ℃, should take appropriate heating measures, or should extend the curing time.

   2, when the ambient temperature is high or larger amount of plastic when the operating time will be shortened.

   3, the goods in a cool dry environment sealed storage, shelf life of 2 years; by non-dangerous goods transport.

   4, the goods are non-dangerous goods, but do not import and eyes, to avoid long-term direct contact with the body.