SNT-801 Small particles Wear-resistant coating

Your current locations: Home >> Products >> Wear-resistant coating

SNT-801 Small particles Wear-resistant coating

  • category:Wear-resistant coating

  • The number of clicks:
  • Release date:2017/09/27
  • Online inquiry
Details

    SNT-801 small particle wear-resistant coating is spherical small particles of ceramic and other filler materials, wear-resistant composite ceramic materials. Two-component, dark gray clay, high bonding strength, wear resistance, corrosion resistance, aging resistance, room temperature curing, heating curing can get better overall performance, moderate viscosity, can be applied to any shape, easy construction.

    SNT-801 small particle wear-resistant coating for fine particle impact conditions on the equipment to repair large area wear or pre-protective coating, such as coal washing ore feeding system piping, elbow, chute, centrifuge scraper drum, vibration Sieve beams, etc .; cement plant mortar pump, ash feeding powder pipeline; power plant desulfurization pipeline.


Product parameters:

name

Colour

status

package

volume

Operating time limit

Curing time

(cm3)

(25℃)

(25℃)

SNT-801

 Small particles

gray

Paste

10kg 

4200

35min

24h

Wear-resistant

 coating

density

Compressive strength

Tensile Strength

Shear strength

Bending strength

hardness

Operating temperature

(g/cm3)

(kg/cm2)

(kg/cm2)

(kg/cm2)

(kg/cm2)

(Shore D)

(℃)


GB1041-2008

GB6329-1999

GB7124-2009

GB1042-2008

ASTM-D-2556


2.37

967

366

223

507

89

-60~160

Instructions:

    1. Surface treatment: roughening the area to be treated, grinding or sandblasting of the grinders, etc.; cleaning the roughened surface; the treated surface should be a coarsened surface of a dry fresh substrate and should No oil, no dust.

    2. Preparation: according to the provisions of the SNT-801 small particles wear-resistant coating A, B two components mixed evenly, and used within 30min. Usually the side of the construction side of the configuration, a configuration of the largest amount can not exceed 1.5 kg, too much solidification of solid too fast, not exhausted has been partially solidified and can not be used. Can be based on the actual temperature in winter may be appropriate with more appropriate summer with less If the temperature is too low, the A component can be properly heated to reduce the viscosity to facilitate the configuration.

    3. Coating: SNT-9021 suitable coating thickness is 3 ~ 10mm, should be mixed with a good material layer by layer in the repair area, the first layer to be compacted, so that with the substrate full infiltration; coating After the size of the surface to be flattened. This material can not be machined, should pay attention to control the coating thickness, so as to avoid interference in the assembly phenomenon; coated with anhydrous ethanol in the surface gently applied, wipe smooth bright side.

    4. Curing: 25 ℃ curing 24 hours can be put into use, if the temperature should be heated or prolonged curing time to promote curing; general winter construction can be used iodine tungsten from the coating 40cm distance irradiation heating.