SNT-855 desulfurization special wear-resistant repair materials used in desulfurization system wear anti-corrosion coating (including desulfurization pump repair coating materials, absorption tower spray layer wear-resistant anti-corrosion coating materials, desulfurization pipeline repair and protective materials, Damaged repair material). SNT-855 is made of high-performance wear-resistant particles (silicon carbide, corundum, etc.) and modified toughening resin composite polymerization of ceramic materials. Two-component, gray clay. Viscosity is moderate, scratch coating easy to apply. Can be cured at room temperature, after curing with the substrate firmly to form a layer of wear resistance, corrosion resistance, impact resistance, anti-cavitation, anti-aging anti-corrosion coating. Repair and Protection of Extinguishing Corrosion Wear for Extinguishing of Desulphurization System. (Including slurry circulation pump shell, impeller repair; gypsum slurry pump shell, impeller repair; slurry mixing tank, stirring pad repair, desulfurization pump inlet pipe, outlet pipe repair, etc.).
Operating time limit
SNT-855 desulfurization special
wear-resistant repair materials
Black and gray paste
Hardness after curing
1. Surface treatment: clean up the site to be repaired impurities, grind grinding or sandblasting roasting; ethyl acetate or acetone cleaning; dry or dry hot air dry.
2. With the plastic: This product is divided into two: 1 and 4: 1 two, the SNT-855 according to the corresponding mass ratio of uniform, and used in 30min. Usually the side of the construction side configuration, a configuration of the largest amount can not exceed 3 kg, a deployment of too much, SNT-855 curing fast, not used up part of the curing can not be used, resulting in waste. According to the construction site temperature suitable for winter with more appropriate summer with less appropriate.
3. Coating: The mixture of uniform desulfurization pump repair coating layer by layer in the repair area, the adhesive layer to be compacted, so that with the substrate fully infiltrated, and to ensure that no holes in the middle. SNT-855 suitable coating thickness is 3 ~ 12mm, wear the workpiece to repair the required size after the surface to be flat. Or brush on the surface of a layer of uniform mixing SNT-865 can be painted ceramic coating.
4. Curing: SNT-855 room temperature 25 ℃ after 48 hours can be put into use, the temperature is lower than 15 ℃, should be in the material after the initial solid iodine tungsten lamp or electric heating plate heated to 80 ℃ for 4 hours to complete curing. Remember not to use fire.
2: 1 30kg / group; plastic drums. A component: 20 kg / barrel, B component: 10 kg / barrel;
4: 1 10kg / group; plastic drums. A component: 8kg / barrel, B component: 2kg / barrel.
Cool and dry place sealed storage, shelf life of 1 year. Transport to avoid inversion, to avoid bumps, according to non-dangerous goods transport