SNT-865 brush type Anti-corrosion anti-corrosion coating

Your current locations: Home >> Products >> Anticorrosive coating

SNT-865 brush type Anti-corrosion anti-corrosion coating

  • category:Anticorrosive coating

  • The number of clicks:
  • Release date:2017/09/27
  • Online inquiry
Details

SNT-865 Brush-type anti-corrosion ceramic coating: two-component, gray fluid, containing high-performance nano-ceramic particles, can be painted to form a smooth wear-resistant anti-corrosion coating. Can be used as wear-resistant particles of rubber gel can also be used alone. Used to repair and pre-protect the eddy current, corrosion, cavitation of the equipment wear. Such as: water cycle equipment surface wear anti-corrosion coating; power plants, ports, water conservancy and hydropower, mining and other industries pump impeller, shell, gate valve surface repair and protection.

Product parameters:


name

Colour

status

package

volume

Operating time limit

Curing time

(cm3)

(25℃)

(25℃)

SNT-865 brush type

Gray, black and blue

Liquid

10kg

4150

45min

24h

Anti-corrosion anti-corrosion coating

density

Compressive strength

Tensile Strength

Shear strength

Bending strength

hardness

Operating temperature

(g/cm3)

(kg/cm2)

(kg/cm2)

(kg/cm2)

(kg/cm2)

(Shore D)

(℃)


GB1041-2008

GB6329-1999

GB7124-2009

GB1042-2008

ASTM-D-2556


1.56

972

396

243

437

81

-60~160

Instructions:


    1. Surface treatment: the need to deal with parts of the coarsening treatment, grinding or sandblasting sand grinder; roughened surface cleaning agent cleaning and drying dry.

    2. Preparation: according to the proportion of the SNT-865 brush-coated anti-corrosion ceramic coating A, B two components by 4: 1 mixed evenly, and run out in 30min.

    3. Coating: The mixed SNT-865 brush-coated ceramic coating is applied to the surface of the treated substrate. The adhesive layer is compacted and impregnated with the substrate.

    4. Curing: 25 ℃ curing 24 hours can be put into use, if the temperature should be heated or prolonged curing time to promote curing; general winter construction can be used iodine tungsten from the coating 40cm distance irradiation heating.


Transport Storage:

     Cool and dry place sealed storage, shelf life of 1 year. Transport to avoid inversion, to avoid bumps, according to non-dangerous goods transport.



Related tags:Acidandalkalianti-corrosioncoating,SNT-865brushtypeAnti-corrosionanti-corrosioncoating價格,SNT-865brushtypeAnti-corrosionanti-corrosioncoating批發